Initial Assessment of 3D-Printed Molybdenum Lattices as a Substrate for Liquid Metal Plasma-Facing Components

Many liquid metal plasma-facing component concepts for fusion reactors require a capillary porous material to wick the liquid metal to the surface of the component. In this work, samples of 3D-printed molybdenum lattices designed to have pore sizes ranging from 100 to 1000 µm were fabricated by two different suppliers. The dimensions of the lattice structures were characterized using an optical microscope, revealing that the lattice walls were almost systematically thicker than they were designed to be and in turn the pores are all smaller than they were designed to be. In many cases the pores were completely clogged. Several spectroscopic techniques were used to characterize the chemical composition of the materials, collectively indicating the presence of a thick layer of oxygen-rich material extending more than 1 µm below the surface. Compression testing revealed significant asymmetry in the mechanical behavior depending on which direction the force was applied relative to the print direction. Lastly, lithium wetting tests of several lattice samples were performed, and a sample with ~250-µm pores was found to soak up lithium quickly after initial wetting of the surface occurred. The implications of these results for future liquid metal plasma-facing component design are discussed.