Computational modeling of mixed oxidation-carburization processes: Part 1

Material Science

• Oxidation Reaction 100%
• Oxide Compound 100%
• Carburization 100%
• Film 25%
• Silicon Dioxide 25%
• Mechanical Strength 25%
• Finite Difference 25%
• Chromium 25%
• Aluminum Oxide 25%
• Nickel-Chromium Alloys 25%
• Oxidant 25%
• Corrosion 25%
• Oxide Film 25%
• Corrosion Resistance 25%
• Point Defect 25%
• Microstructural Evolution 25%
• Superalloys 25%

Engineering

• Oxide Scale 100%
• Subsurface 33%
• Defects 33%
• Initial Stage 33%
• Oxide Film 33%
• Corrosion Resistance 33%
• Aluminum Oxide 33%
• Microstructural Evolution 33%
• Surface Film 33%
• Dissolution Process 33%
• Resistant Alloy 33%
• Carburizing 33%

Keyphrases

• Precipitate Dissolution 100%
• Second-phase Precipitates 50%
• Diffusion Dissolution 50%
• Initial Corrosion 50%
• Point Defect Chemistry 50%
• High Chromium 50%
• Scale Spallation 50%